Title层状Li(Ni_(1-x)Co_x)O_2结构研究
Other TitlesStudy on LiNi1-xCoxO2 structure
Authors谷亦杰
吴惠康
麻向阳
周恒辉
魏清
常文保
Affiliation山东科技大学材料学院
青岛澳柯玛集团有限公司与山东科技大学新能源材料研发中心 青岛266510
青岛澳柯玛集团有限公司与山东科技大学新能源材料研发中心
大同水泥有限公司
北京大学化学与分子工程学院
青岛266510
大同037044
北京100871
Keywords层状L(Ni_(1-x)Co_x)O_2
Ni~(2+)与Li~+有序性
Ni-O八面体
layered Li(Ni1-xCox)O-2
the ordering of Ni2+ in Li+ sites
Ni-O octahedron
Issue Date2006
Publisher无机化学学报
Citation无机化学学报.2006,(03),494-497.
AbstractLiNi1-xCoxO2 with x=0.1, 0.2, 0.3, 0.5 and 1 were prepared by co-precipitation of mixed solution of Ni- and Co-salt in NaOH. The structure of LiNi1-xCoxO2 was analyzed by XRD. The results show that the unit cell constants a and c decrease as the Co content increases. Although the change of unit cell...
LiNi1-xCoxO2 with X=0.1, 0.2, 0.3, 0.5 and 1 were prepared by co-precipitation of mixed solution of Ni-and Co-salt in NaOH. The structure of LiNi1-xCoxO2 was analyzed by XRD. The results show that the unit cell constants a and c decrease as the Co content increases. Although the change of unit cell constants can reflect the substitution of Co ions with Ni ions in the lab, the splits of the pairs of (006), (102) and (108), (110) in the XRD pattern can not reflect the presence of Ni2+ in the lithium site.
URIhttp://hdl.handle.net/20.500.11897/208615
ISSN1001-4861
DOI10.3321/j.issn:1001-4861.2006.03.020
IndexedSCI(E)
中文核心期刊要目总览(PKU)
中国科技核心期刊(ISTIC)
中国科学引文数据库(CSCD)
Appears in Collections:化学与分子工程学院

Files in This Work
Adobe PDF

Web of Science®



Checked on Last Week

Scopus®



Checked on Current Time

百度学术™



Checked on Current Time

Google Scholar™





License: See PKU IR operational policies.